Hardness of weld metal (HV) |
Typical Chemical Composition of All-Weld Metal (wt%) | ||||||||
---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Cr | Mo | W | ||
WT-250H | 255 | 0.07 | 0.50 | 1.58 | 0.018 | 0.011 | 1.30 | 0.002 | - |
Characteristics on Usage | - It is highly recommendable to use on wear plate and weld metal's hardness should be over Hv 250. | ||||||||
WT-350H | 360 | 0.12 | 0.45 | 1.36 | 0.015 | 0.011 | 1.30 | 0.21 | - |
Characteristics on Usage | - It is highly recommendable to use on wear plate and weld metal's hardness should be over Hv 350. | ||||||||
WT-450H | 452 | 0.12 | 0.45 | 1.56 | 0.012 | 0.010 | 3.10 | 0.50 | - |
Characteristics on Usage | - It is highly recommendable to use on wear plate and weld metal's hardness should be over Hv 450. | ||||||||
WT-600H | 605 | 0.34 | 2.10 | 0.50 | 0.013 | 0.008 | 6.50 | 0.51 | - |
Characteristics on Usage | - It is highly recommendable to use on wear plate and weld metal's hardness should be over Hv 600. | ||||||||
WT-700H | 710 | 0.40 | 1.50 | 0.60 | 0.012 | 0.010 | 6.52 | - | 0.80 |
Characteristics on Usage | - It is highly recommendable to use on wear plate and weld metal's hardness should be over Hv 700. | ||||||||
WT-800H | 804 | 0.43 | 1.42 | 0.55 | 0.013 | 0.011 | 7.50 | - | 1.00 |
Characteristics on Usage | - It is highly recommendable to use on wear plate and weld metal's hardness shouldbe over Hv 800. | ||||||||
WT-900B | 900 | 1.63 | 0.44 | 0.64 | 0.011 | 0.02 | 10.5 | 0.05 | B : 6.3 |
Characteristics on Usage |
- Open arc cored wire. - Extremely severe abrasive wear and moderate impact. |
||||||||
WT-H60C-O | 720 | 5.0 | 1.4 | 1.5 | 0.03 | 0.01 | 30 | - | Fe : Bal |
Characteristics on Usage |
- Open arc cored wire. - Extremely severe abrasive wear and moderate impact. |
||||||||
WT-H60B | 750 | 2.5 | 2.5 | 2.4 | 0.02 | 0.004 | 26.9 | 1.0 | 0.39 |
Characteristics on Usage |
- Open arc cored wire. - Extremely severe abrasive wear and moderate impact. |
||||||||
WT-13Mn | 250 | 0.9 | 0.27 | 14.4 | 0.011 | 0.001 | 3.6 | 0.01 | - |
Characteristics on Usage | - Abrasion accompanied by heavy impact parts and repair welding of 13%-Mn cast steel. |