- Applications
- Welding of aluminum-killed steel for low temperature used for LPG tankers and LPG storage tanks.
- Characteristics on Usage
-
- - W 8016G is an extra low hydrogen type electrode for all position welding of aluminum-killed steel and TMCP steel used at low temperature.
- - The weld metal contains about 1.6%Ni.
- - Notch toughness of weld metal at low temperature (-40 ~ -50℃) is stable and good.
- Notes on Usage
-
- - Pay attention not to exceed proper heat-input because excessive causes deterioration of impact values of weld metal.
- - Dry the electrodes at 350~400℃ for about one hour before use.
- - Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blowholes at the arc starting.
- - Keep the arc as short as possible.
- Sizes Available and Recommended Currents ( AC or DC ± )
-
Sizes Available and Recommended Currents ( AC or DC ± )
Size mm (in) |
2.6 (3/32) |
3.2 (1/8) |
4.0 (5/32) |
5.0 (3/16) |
Length mm(in) |
350(14) |
350(14) |
400(16) |
400(16) |
F
| 55~85 |
90~130 |
130~180 |
190~240 |
V-up & OH
| 50~80 |
80~115 |
120~170 |
150~200 |
- Typical Chemical Composition of All-Weld Metal (wt%)
-
Typical Chemical Composition of All-Weld Metal (wt%)
C |
Mn |
Si |
P |
S |
Ni |
0.06 |
1.05 |
0.50 |
0.010 |
0.009 |
1.61 |
- Typical Mechanical Properties of All-Weld Metal
-
Typical Mechanical Properties of All-Weld Metal
Y.S N/mm² |
T.S N/mm² |
EL(%) |
CVN-Impact Value J ( -46℃ ) |
Heat Treatment |
530 |
612 |
29 |
110 |
AW |
511 |
600 |
32 |
120 |
690℃ X 1hr S · R |
- Welding positions