- Applications
- Welding of shells of railway vehicles, cars and other steel sheet structures and general light structural steels.
- Characteristics
-
- - W 6013 is a high titania type electrode which provides good usability in all positions.
- - The arc is stable with little spatter and the lustrous bead can be obtained.
- - W 6013 is suitable for welding steel sheets and light structures because of shallow penetration.
- Notes on Usage
-
- - Pay attention not to exeed the range of proper currents. Welding with excessive current not only lowers X-ray soundness, but also causes increase of spatter, under-cut.
- - Dry the electrodes at 70~100℃ for 30~60 minutes before use. Excessive moisture absorption lowers usability and may result in some porosities.
- Sizes Available and Recommended Currents ( AC or DC ± )
-
Sizes Available and Recommended Currents ( AC or DC ± )
| Dia. (mm) |
2.0 |
2.6 |
3.2 |
4.0 |
5.0 |
6.0 |
| Length (mm) |
300 |
350 |
350 |
400 |
400 |
450 |
Current
(A) |
F |
30~65 |
45~100 |
60~130 |
105~170 |
150~230 |
200~280 |
| V-up & OH |
30~65 |
45~90 |
60~110 |
100~150 |
125~200 |
- |
- Typical Mechanical Properties of All-Weld Metal(%)
-
Typical Mechanical Properties of All-Weld Metal(%)
| C |
Mn |
Si |
P |
S |
| 0.06 |
0.43 |
0.29 |
0.018 |
0.012 |
- Typical Mechanical Properties of All-Weld Metal
-
>Typical Mechanical Properties of All-Weld Metal
| Y.S MPa |
T.S MPa |
EL(%) |
| 430 |
480 |
28 |
- Welding positions
- Approved by
- JIS