- Applications
- W 8016C2 is designed for welding of 3.5%Ni steel(ASTM A203 Gr. D,E) used for pressure vessels, storage tanks.
- Characteristics on Usage
-
- - W 8016C2 is an all positions extra low hydrogen type electrode for 3.5% Ni steel be used at low temperature. (lowest -100℃)
- - Good toughness of all-weld metal at low temperature.
- Notes on Usage
-
- - Preheat at 50~100℃ and postheat at 600~620℃. The preheat temperature varies in accordance with the plate thickness and the kind of steels.
- - Dry the electrodes at 350~400℃ for about one hour before use.
- - Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blowholes at the arc starting.
- - Keep the arc as short as possible.
- Size Available and Recommended Currents ( AC or DC ± )
-
Size Available and Recommended Currents ( AC or DC ± )
Size mm (in) |
2.6 (3/32) |
3.2 (1/8) |
4.0 (5/32) |
5.0 (3/16) |
6.0 (15/64) |
Length mm(in) |
350(14) |
350(14) |
400(16) |
400(16) |
450(18) |
F
| 55~90 |
90~130 |
130~910 |
190~240 |
250~300 |
V-up & OH
| 50~80 |
80~120 |
120~170 |
150~200 |
_ |
- Typical Chemical Composition of All-Weld Metal (wt%)
-
Typical Chemical Composition of All-Weld Metal (wt%)
C |
Mn |
Si |
P |
S |
Ni |
0.05 |
0.54 |
0.38 |
0.010 |
0.009 |
3.52 |
- Typical Mechanical Properties of All-Weld Metal
-
Typical Mechanical Properties of All-Weld Metal
Y.S N/mm² |
T.S N/mm² |
EL (%) |
CVN-Impact Value J ( -75℃ ) |
Heat Treatment |
542 |
628 |
31 |
78 |
620℃ X 1hr S · R |
- Welding positions