- Applications
- Welding of such parts, where the highest reliability is required, such as strength members of ship hulls, high pressure vessels and buildings.
- Characteristics
-
- - W 4301 is ilmenite type covered electrode which is designed for better weldability in particular.
- - Welding of such parts, where the highest reliability is required, such as strength members of ship hulls, high pressure vessels and buildings.
- - W 4301 is lime-titania type electrodes for all-position welding, which has excellent usability. Its crack resistibility and X-ray soundness are excellent.
- - The most excellent mechanical properties and also suitable for welding of structural steels of heavy section about 25mm thickness.
- Notes on Usage
-
- - Pay attention not to exceed the range of proper currents in case of welding structures which require weld metal of high X-ray soundness.
- - Dry the electrodes at 70~100℃ for 30~60 minutes before use. Excessive moisture absorption lowers usability and may result in some porosities.
- - Excessive drying before use causes less penetration and overheating of the electrode.
- Sizes Available and Recommended Currents ( AC or DC ± )
-
Sizes Available and Recommended Currents ( AC or DC ± )
Dia. (mm) |
2.0 |
2.6 |
3.2 |
4.0 |
5.0 |
6.0 |
Length (mm) |
300 |
350 |
350 |
400 |
400 |
450 |
Current (A) |
F |
35~55 |
50~85 |
80~130 |
120~180 |
170~250 |
240~310 |
V-up & OH |
30~50 |
45~70 |
60~110 |
110~150 |
130~200 |
- |
- Typical Chemical Composition of All-Weld Metal (wt%)
-
Typical Chemical Composition of All-Weld Metal (wt%)
C |
Mn |
Si |
P |
S |
0.08 |
0.42 |
0.13 |
0.015 |
0.014 |
- Typical Mechanical Properties of All-Weld-Metal
-
Typical Mechanical Properties of All-Weld-Metal
Y.S MPa |
T.S MPa |
EL(%) |
CVN-Impact Value J (-20℃) |
400 |
470 |
32 |
100 |
- Welding positions