- Applications
- WT-71T9C is designed for welding of 490MPa a low temperature steels.
It can be used in a variety of applications including railcar, automotive, machinery, shipbuilding, bridges, heavy equipment etc.
- Characteristics on Usage
-
- - It is a titania type of flux cored wire for all-position welding.
- - It provides smooth arc, low spatter levels, good weldability and good bead appearance.
- - It design achieves low temperature impacts and can be used in semiautomatic and
automatic applications.
- Notes on Usage
-
- - Proper preheating(50~150℃) and interpass temperature must be used in order to release diffusible hydrogen which may cause cracking in weld metal when electrodes are used for medium and heavy plates.
- - One-side welding defects such as hot cracking may occur with wrong welding parameter such as high welding speed.
- - Gas flow rate is proper 20~25ml.
- - Shielding gas should be used 100% CO2.
- Sizes Available and Recommended Currents ( DC + )
-
Sizes Available and Recommended Currents ( DC + )
Dia(mmØ) |
1.2 |
1.4 |
1.6 |
Position |
F |
Amp |
180~340A |
200~360A |
200~420A |
HF |
180~340A |
200~360A |
200~420A |
V-up, OH |
120~220A |
140~260A |
160~280A |
- Typical Chemical Composition of All-Weld-Metal (wt%) (Shielding gas : CO2)
-
Typical Chemical Composition of All-Weld-Metal (wt%)
C |
Mn |
Si |
P |
S |
Ni |
0.03 |
1.4 |
0.38 |
0.011 |
0.003 |
0.30 |
- Typical Mechanical Properties of All-Weld-Metal (Shielding gas : CO2)
-
Typical Mechanical Properties of All-Weld-Metal
Y.S MPa |
T.S MPa |
EL(%) |
CVN-Impact Value J (-30℃) |
491 |
545 |
33 |
120 |
- Welding position