- Applications
- WT-100K3 is designed for welding of 690MPa high tensile steel for low temperature service.
Typical applications include pipe line, wear resistance steel such as API 5L, X70, X80, EN 10208-2 L480, L550, EN 10137-2 S550, S620.
- Characteristics on Usage
-
- - Wire is a titania type of flux cored wire for flat and horizontal position welding.
- - It provides smooth arc, low spatter levels, good weldability and good bead appearance.
- Notes on Usage
-
- - Proper preheating(50~150℃) and interpass temperature must be used in order to release diffusible hydrogen which may cause cracking in weld metal when electrodes are used for medium and heavy plates.
- - Gas flow rate is proper 20~25â„“/min.
- - Shielding gas should be used 100% CO2.
- Sizes Available and Recommended Currents ( DC + )
-
Sizes Available and Recommended Currents ( DC + )
Dia(mmØ) |
1.2 |
1.4 |
1.6 |
Position |
F |
Amp |
180~340A |
200~360A |
200~420A |
HF |
180~340A |
200~360A |
200~420A |
- Typical Chemical Composition of All-Weld-Metal (wt%) ( Shielding gas : MIX)
-
Typical Chemical Composition of All-Weld-Metal (wt%)
C |
Mn |
Si |
P |
S |
Ni |
Mo |
0.04 |
1.35 |
0.40 |
0.011 |
0.005 |
2.04 |
0.38 |
- Typical Mechanical Properties of All-Weld-Metal( Shielding gas : MIX)
-
Typical Mechanical Properties of All-Weld-Metal
Y.S MPa |
T.S MPa |
EL(%) |
CVN-Impact Value J (-20℃) |
682 |
712 |
20 |
125 |